Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA A-1565HS BK324 SOLVAY USA
AMODEL®
Automotive components、Sports equipment、Parts under the hood of a、Pump parts、Shell、Application in the automo、Industrial applications、Industrial components
High temperature resistan、Flame retardant、Thermal stability、Filler: Glass mineral、65% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/A-1565HS BK324 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 32 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 44 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/A-1565HS BK324 |
|---|---|---|---|
| Tensile modulus | 175°C | ISO 527-2 | 5100 Mpa |
| compressive strength | 13.0mm | ASTM D695 | 189 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 19700 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 138 Mpa |
| 断裂,24°C | ISO 527-2 | 91.7 Mpa | |
| bending strength | 175°C | ISO 178 | 55.8 Mpa |
| Flexural modulus | ASTM D790 | 17900 Mpa | |
| Tensile modulus | 150°C | ISO 527-2 | 5720 Mpa |
| bending strength | 150°C | ISO 178 | 69.6 Mpa |
| 100°C | ISO 178 | 163 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.2 % |
| tensile strength | 断裂,150°C | ISO 527-2 | 46.2 Mpa |
| Flexural modulus | 23°C | ISO 178 | 9100 Mpa |
| Tensile strain | 断裂,150°C | ISO 527-2 | 2.4 % |
| bending strength | ASTM D790 | 210 Mpa | |
| Flexural modulus | 100°C | ISO 178 | 6830 Mpa |
| Tensile strain | 断裂,175°C | ISO 527-2 | 1.8 % |
| tensile strength | 断裂,175°C | ISO 527-2 | 32.4 Mpa |
| Tensile modulus | 100°C | ISO 527-2 | 15400 Mpa |
| tensile strength | ASTM D638 | 131 Mpa | |
| Tensile strain | 断裂,24°C | ISO 527-2 | 1.3 % |
| Tensile modulus | ASTM D638 | 20700 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.0 % |
| Flexural modulus | 150°C | ISO 178 | 2480 Mpa |
| bending strength | 23°C | ISO 178 | 211 Mpa |
| Flexural modulus | 175°C | ISO 178 | 2280 Mpa |
| shear strength | ASTM D732 | 71.0 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/A-1565HS BK324 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 4E+14 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | V |
| arc resistance | ASTM D495 | 125 sec |
| physical property | Test Condition | Test Method | SOLVAY USA/A-1565HS BK324 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30 % |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| Shrinkage rate | TD | ASTM D955 | 0.50 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/A-1565HS BK324 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 311 °C | |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 8.1E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 271 °C |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 1.7E-05 cm/cm/°C |
| TD：0to100°C | ASTME831 | 3.7E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 271 °C |
| melting temperature | ASTM D3418 | 311 °C | |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2E-05 cm/cm/°C |