Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CM6240-701 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electronic and electrical、Automotive components、Plate
High mobility、Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6240-701 |
|---|---|---|---|
| Dart impact | -30°C, Total Energy | ASTM D3763 | 35.0 J |
| 23°C, Total Energy | ASTM D3763 | 56.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6240-701 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 4350 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 29.0 Mpa |
| 屈服3 | ASTM D638 | 55.0 Mpa | |
| elongation | 断裂3 | ASTM D638 | 35 % |
| Flexural modulus | --5 | ISO 178 | 4510 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 96.0 Mpa |
| --5,6 | ISO 178 | 101 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 4400 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 3.0 % |
| tensile strength | 屈服 | ISO 527-2/5 | 56.0 Mpa |
| elongation | 屈服3 | ASTM D638 | 3.0 % |
| tensile strength | 断裂3 | ASTM D638 | 40.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 4460 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 25 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6240-701 |
|---|---|---|---|
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| 1.5 mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6240-701 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.030 % |
| Shrinkage rate | 横向流动 | 内部方法 | 0.38 % |
| Melt volume flow rate | 260°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| Shrinkage rate | 流动 | 内部方法 | 0.33 % |
| melt mass-flow rate | 260°C/2.16 kg | ASTM D1238 | 17 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.30 - 0.40 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6240-701 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 4.9E-5 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 100 °C |
| -- | ASTM D15259 | 97.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 6.3E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 4.8E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 90.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 86.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 6.4E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6240-701 |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.040 % | ||
| Temperature in the middle of the barrel | 230 to 275 °C | ||
| Temperature at the rear of the barrel | 220 to 255 °C | ||
| Processing (melt) temperature | 255 to 285 °C | ||
| drying temperature | 80 to 90 °C | ||
| Temperature at the front of the material cylinder | 255 to 285 °C | ||
| Temperature | 70 to 95 °C | ||
| Spray nozzle temperature | 255 to 285 °C |