Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PPO HS2000X-111 SABIC INNOVATIVE SHANGHAI

NORYL™

Swimming Pool Facilities,Electronic and Electrical Applications,Air conditioning accessories,Shell,Smoke detector cover,Water pump accessories,Indoor applications,Outdoor applications

Glass fiber mineral reinf,Dimensional stability,Low water absorption

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/HS2000X-111
0.45MPa, unannealed, 100mm span		ISO 75-2/Be	126 °C
0.45MPa, unannealed, 3.20mm		ASTM D648	117 °C
0.45MPa, unannealed, 6.40mm		ASTM D648	128 °C
1.8MPa, unannealed, 100mm span		ISO 75-2/Ae	111 °C
1.8MPa, unannealed, 3.20mm		ASTM D648	108 °C
1.8MPa, unannealed, 6.40mm		ASTM D648	116 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.1E-05 cm/cm/°C
Linear coefficient of thermal expansion		TD:-40to40°C	ASTME831	7.8E-05 cm/cm/°C
RTI		UL 746	100 °C
RTI Elec		UL 746	100 °C
RTI Imp		UL 746	85.0 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/HS2000X-111
--1		ASTM D638	3650 Mpa
100mm span 5	100mm	ASTM D790	3550 Mpa
50.0mm span		ASTM D790	3670 Mpa
crack		ASTM D638	60.0 Mpa
			ASTM D638	8.4 %
			ISO 527-2	11 %
			ISO 527-2	57.1 Mpa
Fracture, 50.0mm span		ASTM D790	117 Mpa
yield		ASTM D638	3.8 %
			ASTM D638	74.0 Mpa
			ISO 527-2	3.7 %
			ISO 527-2	71.7 Mpa
Yield, 100mm span		ASTM D790	117 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/HS2000X-111
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Dielectric constant	1MHz	ASTM D150	2.70
		50Hz	ASTM D150	2.89
		60Hz	ASTM D150	2.89
Dielectric strength	3.20mm,inOil	ASTM D149	17 KV/mm
Dissipation factor	1MHz	ASTM D150	4.4E-03
		60Hz	ASTM D150	0.017
		50Hz	ASTM D150	0.017
High arc combustion index	HAI	UL 746	PLC 2
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 0
Surface resistivity		ASTM D257	>1.0E+16 ohms
Volume resistivity		ASTM D257	1.2E+16 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/HS2000X-111
melt mass-flow rate	280°C/5.0kg	ASTM D1238	7.6 g/10min
melt mass-flow rate		300°C/5.0kg	ASTM D1238	7.6 g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	6.80 cm3/10min
Melt Volume Flow Rate (MVR)		300°C/5.0kg	ISO 1133	6.80 cm3/10min
Outdoor applicability		UL 746C	f1
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/HS2000X-111
23°C		ASTM D256	130 J/m
23°C			ISO 180/1A	9.7 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	443 J
Reverse notch impact	3.20mm	ASTM D256	810 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2200 J/m

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/HS2000X-111
UL flame retardant rating	1.47mm	UL 94	V-0
		RadiantPanelListing(UL)	UL 94	YES
		2.01mm	UL 94	5VA