PA66 HTNFE8200 DUPONT USA
Zytel® 
Electrical applications,Automotive Applications
Glass fiber reinforced,high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT USA/HTNFE8200
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
23°CISO 179/1eUNoBreak
thermal performanceTest ConditionTest MethodDUPONT USA/HTNFE8200
Heat Deflection Temperature1.8MPa,未退火，HDTISO 75-2/A126 °C
0.45MPa,未退火，HDTISO 75-2/B138 °C
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-29E-05 cm/cm/°C
MD：--ISO 11359-29E-05 cm/cm/°C
MD：-40to23°CISO 11359-29E-05 cm/cm/°C
TD：--ISO 11359-21E-04 cm/cm/°C
melting temperatureISO 11357-3300 °C
mechanical propertiesTest ConditionTest MethodDUPONT USA/HTNFE8200
Nominal tensile fracture strainISO 527-214 %
Poisson's ratioISO 5270.38
Tensile modulusISO 527-22200 Mpa
tensile strength屈服ISO 527-268.0 Mpa
Tensile strain屈服ISO 527-25.5 %
flexural modulusISO 1782100 Mpa
Electrical performanceTest ConditionTest MethodDUPONT USA/HTNFE8200
volume resistivityIEC 600931E+15 ohms·cm
Surface ResistivityIEC 60093-- ohms
Physical propertiesTest ConditionTest MethodDUPONT USA/HTNFE8200
Water absorption rate平衡,23°C,2.00mm,50%RHISO 621.9 %
ThermalConductivityofMelt0.18 W/m/K
SpecificHeatCapacity of Melt2220 J/kg/°C
shrinkage rateTDISO 294-40.90 %
MediumDensity0.970 g/cm³
Ejection Temperature225 °C
Water absorption rate饱和,23°C,2.00mmISO 626.3 %
shrinkage rateMDISO 294-40.80 %
flammabilityTest ConditionTest MethodDUPONT USA/HTNFE8200
UL flame retardant rating0.75mmUL 94HB
0.75mmIEC 60695-11-10,-20HB
1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
UL flame retardant rating1.5mmUL 94HB
burning rate1.00mmISO 3795<100 mm/min