LLDPE Trademark PE LLH1918 Trademark Plastics Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LLH1918 |
|---|---|---|---|
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709 | 210 g |
| Elmendorf tear strength | TD:25µm,吹塑薄膜 | ASTM D1922 | 630 g |
| elongation | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 690 % |
| Secant modulus | 1%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 203 MPa |
| Elmendorf tear strength | MD:25µm,吹塑薄膜 | ASTM D1922 | 350 g |
| film thickness | 25 µm | ||
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 42.1 MPa |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 580 % |
| Secant modulus | 1%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 221 MPa |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 55.8 MPa |
| optical performance | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LLH1918 |
|---|---|---|---|
| Haze ratio | 25.4µm,吹塑薄膜 | ASTM D1003 | 19 % |
| gloss | 45°,25.4µm,吹塑薄膜 | ASTM D2457 | 35 |
| physical property | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LLH1918 |
|---|---|---|---|
| density | ASTM D1505 | 0.918 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |