PA66 TSG-30/4 V0 EMS-CHEMIE SWITZERLAND
Grilon® 
Automotive Applications
Thermal stability,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Other performanceTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSG-30/4 V0
Flammability levelUL 94干燥|V-0
thermal performanceTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSG-30/4 V0
Continuous use temperature--3ISO 2578干燥|100 -120 °C
--4Internal Method干燥|220 °C
Hot deformation temperature8.0 MPa, UnannealedISO 75-2/C干燥|165 °C
1.8 MPa, UnannealedISO 75-2/A干燥|235 °C
Melting temperatureISO 11357-3干燥|260 °C
mechanical propertiesTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSG-30/4 V0
Ball Pressure TestISO 2039-1调节后|130 Mpa
Charpy Notched Impact Strength-30°CISO 179/1eA调节后|8.5 kJ/m²
23°CISO 179/1eA调节后|14 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU调节后|60 kJ/m²
23°CISO 179/1eU调节后|70 kJ/m²
Tensile modulusISO 527-2调节后|6500 Mpa
Tensile strainBreakISO 527-2调节后|4.5 %
tensile strengthBreakISO 527-2调节后|90.0 Mpa
Electrical performanceTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSG-30/4 V0
Compared to the anti leakage trace indexIEC 60112 V
Dielectric strengthIEC 60243-1调节后|26 KV/mm
Surface resistivityIEC 60093调节后|1.0E+10 ohms
Volume resistivityIEC 60093干燥|1.0E+12 ohms·cm
Physical propertiesTest ConditionTest MethodEMS-CHEMIE SWITZERLAND/TSG-30/4 V0
Shrinkage rateMDISO 294-4干燥|0.20 %
TDISO 294-4干燥|0.70 %
Water absorption rateSaturation, 23°CISO 62干燥|4.0 %
Equilibrium, 23°C, 50% RHISO 62干燥|1.5 %