PBT 1101H TORAY JAPAN
Toraycon®
Shell
Good appearance、Mineral reinforcement
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 150 °C |
| 0.45MPa,未退火 | ISO75-2/B | 150 °C | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 75.0 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 75.0 °C |
| Hardness | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Rockwell Hardness | M计秤,23°C | ISO2039-2 | 80 |
| Physical | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Modeling Shrinkage | TD:3.00mm2 | 内部方法 | 1.7 % |
| TD: 3.00 mm | Internal Method | 1.7 % | |
| MD: 3.00 mm | 1.8 % | ||
| MD:3.00mm4 | 内部方法 | 1.8 % |
| Mechanical Properties | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 20 kJ/m² |
| Rockwell Hardness | M 计秤 | ISO 2039-2 | 80 |
| Flexural Strength | 23℃ | ISO 178 | 100 Mpa |
| Tensile Strain | 断裂, 23℃ | ISO 527-2 | 1.8 % |
| Tensile Modulus | 23℃ | 4600 Mpa | |
| Tensile Strain | 断裂,23°C | ISO527-2 | 1.8 % |
| Flexural Modulus | 23°C | ISO178 | 4300 Mpa |
| Tensile Stress | 屈服, 23℃ | ISO 527-2 | 55.0 Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 4600 Mpa |
| Tensile Stress | 屈服,23°C | 55.0 Mpa | |
| Flexural Modulus | 23℃ | ISO 178 | 4300 Mpa |
| Flexural Stress | 23°C | ISO178 | 100 Mpa |
| Impact Properties | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 20 kJ/m² |
| Flammability | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Flame Rating | UL94 | HB |