Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PUR-PC Ultralast™ PR930 CHEMTURU USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PR930 |
|---|---|---|---|
| Shore hardness | 邵氏A | ASTM D2240 | 91to93 |
| Supplementary Information | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PR930 |
|---|---|---|---|
| Dynamic Properties | TangentDelta:30°C | 0.0520 | |
| StorageModulus:140°C | 1.49E+08 dynes/cm² | ||
| StorageModulus:30°C | 1.95E+08 dynes/cm² | ||
| TangentDelta:140°C | 0.0290 |
| film | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PR930 |
|---|---|---|---|
| Tear resistance of pants | ASTM D1938 | 105 N/mm |
| Mechanical properties | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PR930 |
|---|---|---|---|
| Wear resistance - DIN | DIN 53516 | 26.0 mm³ | |
| Flexural modulus | ASTM D790 | 41.4 MPa |
| physical property | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PR930 |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ASTM D955 | 1.4 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 50to80 g/10min |
| density | ASTM D792 | 1.18 g/cm³ | |
| Shrinkage rate | MD:24小时 | ASTM D955 | 1.5 % |
| elastomer | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PR930 |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 530 % |
| tear strength | 开裂 | ASTM D470 | 35 kN/m |
| Shore hardness | ASTM D2632 | 46 % | |
| tensile strength | ASTM D412 | 40.3 MPa | |
| compression set | 100°C,70hr | ASTM D395B | 36 % |
| tear strength | 开裂2 | ASTM D470 | 31 kN/m |
| tensile strength | 100%应变 | ASTM D412 | 10.2 MPa |
| tear strength | 开裂3 | ASTM D470 | 34 kN/m |
| 开裂4 | ASTM D470 | 38 kN/m |
| Thermal performance | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PR930 |
|---|---|---|---|
| vicat | ASTM D1525 | 165 °C | |
| Glass Transition Temperature | -29.0 °C |