PA6 PF1006I BK SABIC INNOVATIVE US

LNP™ THERMOTUF™

Fitness equipment,Plastic bag,Electronic and Electrical Applications

Thermal stability,Glass fiber reinforced,Antistatic,Filler: Glass fiber reinf,30% filler by weight

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/PF1006I BK
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	137 °C
		1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	135 °C
		0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	141 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	139 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/PF1006I BK
Bending modulus	50.0mmSpan	ASTM D790	6830 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	158 Mpa
elongation	Break	ASTM D638	8.2 %
Tensile modulus		ISO 527-2/1	9650 Mpa
Tensile modulus			ASTM D638	16200 Mpa
tensile strength	Break	ISO 527-2/5	99.0 Mpa
		Yield	ASTM D638	50.0 Mpa
		Yield	ISO 527-2/5	35.0 Mpa
		Break	ASTM D638	97.4 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/PF1006I BK
Shrinkage rate	TD：24hr	ASTM D955	0.90-2.0 %
		TD:24hr	ISO 294-4	0.62-0.67 %
		MD:24hr	ISO 294-4	0.11-0.30 %
		MD：24hr	ASTM D955	0.10-0.30 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.83 %
Water absorption rate		24hr,50%RH	ASTM D570	0.83 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/PF1006I BK
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	16.0 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	11 kJ/m²
Multi axis Instrumented Impact Energy		ISO 6603-2	4.98 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	54 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/PF1006I BK
UL flame retardant rating	1.5mm	UL 94	HB