Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS C-140HC IDEMITSU JAPAN
--
--
High mobility、Filler: Glass fiber reinf、40% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 14 kJ/m² |
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 102 |
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| Flowability2 | 1.00mm，Flowability | 内部方法 | 176 mm |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| bending strength | ISO 178 | 262 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | ISO 178 | 14700 Mpa | |
| tensile strength | ISO 527-2 | 179 Mpa |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| dielectric constant | IEC 60250 | 3.90 | |
| dielectric strength | 3.00mm | IEC 60243-1 | 13 KV/mm |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| UL flame retardant rating | 0.750mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.70 % |
| MD | ISO 294-4 | 0.40 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | >0.020 % |
| density | ISO 1183 | 1.65 g/cm³ |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/C-140HC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 272 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 4E-05 cm/cm/°C |