Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS MG47F NA1001 SABIC INNOVATIVE SAUDI
CYCOLAC™
Toy、Office supplies、Automotive Applications、Electrical applications
High impact resistance、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| Impact strength of simply supported beam gap 6 | 23°C | ISO 179/1eA | 26 kJ/m² |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 30.0 J |
| Impact strength of simply supported beam gap 6 | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 47.0 Mpa |
| Bending stress | -- 4, 5 | ISO 178 | 70.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 25 % |
| Tensile modulus | -- 1 | ASTM D638 | 2270 Mpa |
| tensile strength | 屈服 2 | ASTM D638 | 44.0 Mpa |
| elongation | 屈服 2 | ASTM D638 | 2.0 % |
| Flexural modulus | -- 4 | ISO 178 | 2200 Mpa |
| Bending stress | 屈服, 50.0 mm 跨距 3 | ASTM D790 | 70.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 35.0 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 2.6 % |
| Flexural modulus | 50.0 mm 跨距 3 | ASTM D790 | 2300 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2370 Mpa |
| tensile strength | 断裂 2 | ASTM D638 | 33.0 Mpa |
| elongation | 断裂 2 | ASTM D638 | 24 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| ASTM D495 | PLC 6 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| melt viscosity | 240°C, 1000 sec^-1 | ASTM D3835 | 225 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8 kg | ASTM D1238 | 5.6 g/10 min |
| 220°C/10.0 kg | ISO 1133 | 18 g/10 min | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 100 °C |
| -- | ASTM D15258 | 99.0 °C | |
| 横向 : -40 到 40°C | ASTM E831 | 8.8E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 80.0 °C |
| vicat | -- | ISO 306/B50 | 98.0 °C |
| 流动 : -40 到 40°C | ASTM E831 | 8.8E-5 cm/cm/°C | |
| RTI Imp | UL 746 | 60.0 °C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 94.0 °C |
| RTI | UL 746 | 60.0 °C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 81.0 °C |
| RTI Elec | UL 746 | 60.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/MG47F NA1001 |
|---|---|---|---|
| Processing (melt) temperature | 220 到 260 °C | ||
| drying temperature | 80 到 95 °C | ||
| Exhaust hole depth | 0.038 到 0.051 mm | ||
| Temperature at the front of the material cylinder | 215 到 240 °C | ||
| Suggested maximum moisture content | 0.10 % | ||
| Temperature in the middle of the barrel | 205 到 225 °C | ||
| Temperature | 50 到 70 °C | ||
| screw speed | 30 到 60 rpm | ||
| Temperature at the rear of the barrel | 190 到 210 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 2.0 到 4.0 hr | ||
| Suggested injection volume | 50 到 70 % | ||
| Spray nozzle temperature | 220 到 260 °C |