Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT ENH4560 BK1066 SABIC INNOVATIVE NANSHA
VALOX™ 
Plastic bag、Automotive External Parts
Flame retardant、Bromine free、Chlorine free
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
23°CISO 180/1A9.0 kJ/m²
0°CASTM D25675 J/m
23°CISO 180/1U37 kJ/m²
ASTM D25675 J/m
-30°CASTM D25675 J/m
ASTM D4812500 J/m
23°CASTM D4812500 J/m
-30°CISO 180/1A9.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/2U40 kJ/m²
0°CISO 180/1A9.0 kJ/m²
-30°CISO 180/1U37 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/2U35 kJ/m²
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
Rockwell hardnessR计秤ISO 2039-2120
ball-indentation hardnessH358/30ISO 2039-1142 Mpa
Supplementary InformationTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
fillerASTM D22930 %
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
yieldASTM D638110 Mpa
fractureISO 527-2/5105 Mpa
yieldASTM D6382.0 %
Yield, 50.0mm spanASTM D790150 Mpa
yieldISO 527-2/5105 Mpa
ISO 527-2/52.0 %
fractureASTM D638110 Mpa
ASTM D6382.0 %
--8ISO 178170 Mpa
Fracture bending strainISO 1782.0 %
50.0mm spanASTM D7909000 Mpa
--1ASTM D63811000 Mpa
fractureISO 527-2/52.0 %
--7ISO 17810000 Mpa
Fracture, 50.0mm spanASTM D790150 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
1.60mm, In oilIEC 60243-122 KV/mm
Volume resistivityASTMD2571E+14 ohms·cm
dielectric constant1MHzASTMD1503.80
High arc combustion index (HAI)HAIUL 746PLC 0
Dissipation Factor1MHzASTMD1500.14
3.20mm, In oilIEC 60243-118 KV/mm
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
0.800mm, In oilIEC 60243-132 KV/mm
0.800mm, inoilASTM D14932 KV/mm
Hot wire ignition (HWI)HWIUL 746PLC 0
16mm, inoylASTM D14922 KV/mm
Surface ResistivityIEC 60093>1.0E+15 ohms
3.20mm, inoilASTM D14918 KV/mm
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 0
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
UL flame retardant rating3.00mmUL 945VB
Hot filament ignition temperature2.00mmIEC 60695-2-13750 °C
Burning wire flammability index2.00mmIEC 60695-2-12960 °C
UL flame retardant rating0.800mmUL 94V-0
Hot filament ignition temperature3.00mmIEC 60695-2-13800 °C
1.00mmIEC 60695-2-13750 °C
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
melt viscosity260°C,1500sec^-1ISO 11443110 Pa·s
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
melt mass-flow rate265°C/5.0kgASTM D123823 g/10min
Melt volume flow rate250°C/5.0kgISO 113316.0 cm3/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ENH4560 BK1066
Linear coefficient of thermal expansionTD:23到150°CISO 11359-21.5E-04 cm/cm/°C
MD:-40到40°CISO 11359-22E-05 cm/cm/°C
0.45MPa, Unanealed, 64.0mm spanISO 75-2/Bf225224 °C
RTI ImpUL 746125 °C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af210 °C
Linear coefficient of thermal expansionMD:23到150°CISO 11359-22.5E-05 cm/cm/°C
RTIUL 746140 °C
1.8MPa, Unanealed, 3.20mmASTM D648210 °C
0.45MPa, Unanealed, 3.20mmASTM D648223 °C
ball-indentation hardness125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionTD:-40到40°CISO 11359-26.2E-05 cm/cm/°C
RTI ElecUL 746140 °C