PC/ABS NS0031 SABIC INNOVATIVE US
LNP™ FARADEX™
Casters,Electrical applications
High mobility,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/NS0031 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 32 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.5 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 15.0 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/NS0031 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+04 ohms·cm | |
| Surface Resistivity | ASTM D257 | 10to1.0E+3 ohms | |
| Shielding effectiveness (EMI) | 3.00mm | 内部方法 | 50to65 dB |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/NS0031 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2700 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.3 % |
| bending strength | ASTM D790 | 89.6 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 3.5 % |
| tensile strength | 断裂 | ASTM D638 | 49.6 Mpa |
| 断裂 | ISO 527-2 | 46.0 Mpa | |
| Flexural modulus | ASTM D790 | 2990 Mpa | |
| Tensile modulus | ASTM D638 | 3110 Mpa | |
| elongation | 断裂 | ASTM D638 | 4.7 % |
| bending strength | ISO 178 | 86.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 6.0 % |
| Flexural modulus | ISO 178 | 2800 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 52.4 Mpa |
| 屈服 | ISO 527-2 | 50.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/NS0031 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.30 % |
| MD：24小时 | ASTM D955 | 0.30 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.10 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.35 % |
| TD:24小时 | ISO 294-4 | 0.35 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/NS0031 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 115 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 8.2E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 7.7E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 120 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 5.9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 103 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 105 °C |