Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DFL-4022 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Casters,Electronic and Electrical Applications
Easy to demould,Easy to form
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| 0.45MPa, unannealed, 3.20mm | ASTM D648 | 145 °C | |
| 0.45MPa, unannealed, 64.0mm span | ISO 75-2/Bf | 146 °C | |
| 1.8MPa, unannealed, 3.20mm | ASTM D648 | 140 °C | |
| 1.8MPa, unannealed, 64.0mm span of | ISO 75-2/Af | 140 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 5.6E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 5.6E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| --1 | ASTM D638 | 4140 Mpa | |
| bending strength | ISO 178 | 118 Mpa | |
| crack | ASTM D638 | 67.6 Mpa | |
| ISO 527-2 | 67.0 Mpa | ||
| ASTM D638 | 5.5 % | ||
| ISO 527-2 | 5.8 % | ||
| Friction coefficient | 与自身-动态 | ASTM D3702Modified | 0.38 |
| 与自身-静态 | ASTM D3702Modified | 0.44 | |
| Wear factor | Washer | ASTM D3702Modified | 166 10^-10in^5-min/ft-lb-hr |
| yield | ASTM D638 | 71.7 Mpa | |
| ISO 527-2 | 71.0 Mpa | ||
| ASTMD638 | 3.3 % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| Flow: 24 hours | 24小时 | ASTM D955 | 0.40to0.60 % |
| Flow direction: 24 hours | 流动方向, 24小时 | ISO 294-4 | 0.50 % |
| Lateral flow: 24 hours | 横向, 24小时 | ASTM D955 | 0.60to0.80 % |
| Vertical flow direction: 24 hours | 垂直方向, 24小时 | ISO 294-4 | 0.65 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.10 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| 23°C | ASTM D256 | 140 J/m | |
| ASTM D4812 | 740 J/m | ||
| ISO 180/1U | 49 kJ/m² | ||
| ISO 180/1A | 13 kJ/m² | ||
| 23°C,EnergyatPeakLoad | ASTM D3763 | 23.2 J |