PP J-2000GP PRIME POLYMER JAPAN
PRIME POLYPRO 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodPRIME POLYMER JAPAN/J-2000GP
Heat Deflection Temperature0.45MPa,未退火ISO75-2/B93.0 °C
HardnessTest ConditionTest MethodPRIME POLYMER JAPAN/J-2000GP
Rockwell HardnessR计秤ISO2039-299
Mechanical PropertiesTest ConditionTest MethodPRIME POLYMER JAPAN/J-2000GP
Breaking tensile strainISO 527-233 %
Tensile Elongation (Break)简支梁缺口冲击强度，23℃ISO 1793.1 kJ/m²
Tensile ModulusISO 527-21450 Mpa
Tensile Stress屈服ISO527-234.0 Mpa
Flexural ModulusISO 1781450 Mpa
Tensile Stress(Yield)ISO 527-234 Mpa
Tensile Elongation (Break)ISO 527-250 %
洛氏硬度ISO 2039-299
Flexural ModulusISO1781450 Mpa
Tensile Strain断裂ISO527-233 %
Nominal Tensile Strain at BreakISO527-250 %
Flexural StressISO17842.0 Mpa
Tensile ModulusISO527-21450 Mpa
Flexural StrengthISO 17842 Mpa
PhysicalTest ConditionTest MethodPRIME POLYMER JAPAN/J-2000GP
Modeling Shrinkage内部方法1.4到1.8 %
Internal Method1.4-1.8 %
Melt Mass-Flow Rate230°C/2.16kgISO113321 g/10min
Melt index230℃,2.16kgISO 113321 g/10min
OpticalTest ConditionTest MethodPRIME POLYMER JAPAN/J-2000GP
GlossASTMD245780
Impact PropertiesTest ConditionTest MethodPRIME POLYMER JAPAN/J-2000GP
Charpy Unnotched Impact Strength23°CISO1793.1 kJ/m²
Tensile Elongation (Break)Test ConditionTest MethodPRIME POLYMER JAPAN/J-2000GP
Thermal Properties热变形温度，0.45MPa,未退火ISO 75-2/B93 °C
optical performance 光滑面JIS Z874180