Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 6 NV 12FR A SCHULMAN USA
SCHULAMID®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/6 NV 12FR |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/6 NV 12FR |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 4.0 % |
| Tensile modulus | ISO 527-2/1A/1 | 4200 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 70.0 Mpa |
| Electrical performance | Test Condition | Test Method | A SCHULMAN USA/6 NV 12FR |
|---|---|---|---|
| Hot wire ignition (HWI) | 76.2mm | UL 746 | PLC 0 |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 19.1mm | UL 746 | PLC 0 |
| 38.1mm | UL 746 | PLC 0 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 2 |
| 0.75mm | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | A SCHULMAN USA/6 NV 12FR |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | V-0 |
| 0.75mm | UL 94 | V-0 | |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 3.0mm | UL 94 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| 0.38mm | IEC 60695-11-10,-20 | V-0 | |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| burning rate | 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| Hot filament ignition temperature | 0.38mm | IEC 60695-2-13 | 750 °C |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| 0.38mm | IEC 60695-2-12 | 960 °C | |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 750 °C |
| burning rate | 0.750mm,Self-Extinguishing | ISO 3795 | 0.0 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 36 % | |
| burning rate | 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| physical property | Test Condition | Test Method | A SCHULMAN USA/6 NV 12FR |
|---|---|---|---|
| viscosity number | ISO 307 | 130 cm³/g |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/6 NV 12FR |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 95.0 °C |
| RTI Imp | 1.5mm | UL 746 | 75.0 °C |
| RTI Elec | 3.0mm | UL 746 | 130 °C |
| RTI Imp | 3.0mm | UL 746 | 80.0 °C |
| RTI Elec | 0.75mm | UL 746 | 130 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 90.0 °C |
| RTI Imp | 0.75mm | UL 746 | 75.0 °C |
| ball-indentation hardness | 200°C | IEC 60695-10-2 | Pass |
| vicat | -- | ISO 306/A50 | 218 °C |
| RTI Str | 1.5mm | UL 746 | 95.0 °C |
| vicat | -- | ISO 306/B50 | 203 °C |
| RTI Str | 3.0mm | UL 746 | 95.0 °C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 200 °C |