Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA PA GF 60 NA AKRO-PLASTIC GERMANY
AKROLOY®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/PA GF 60 NA |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| -30°C | ISO 179/1eU | 90 kJ/m² |
| hardness | Test Condition | Test Method | AKRO-PLASTIC GERMANY/PA GF 60 NA |
|---|---|---|---|
| ball-indentation hardness | H 961/30 | ISO 2039-1 | 330 Mpa |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/PA GF 60 NA |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 21000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 275 Mpa |
| bending strength | ISO 178 | 405 Mpa | |
| Flexural modulus | ISO 178 | 20000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.5 % |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/PA GF 60 NA |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/PA GF 60 NA |
|---|---|---|---|
| burning rate | 1.00 mm | FMVSS 302 | < 100 mm/min |
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 650 °C |
| filler content | ISO 1172 | 60 % | |
| UL flame retardant rating | 0.8 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GERMANY/PA GF 60 NA |
|---|---|---|---|
| spiral flow length | 内部方法 | 47.0 CM | |
| Humidity Absorption - 62% RH | 70°C | ISO 1110 | 0.80 % |
| Shrinkage rate | 流量 | ISO 294-4 | < 0.30 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 3.0 to 3.5 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 0.50 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/PA GF 60 NA |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 245 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 5.5E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 1.5E-5 cm/cm/°C | |
| Temperature index - at 50% loss of tensile strength | 140 to 150 °C | ||
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 225 °C |
| melting temperature | DIN EN 11357-1 | 255 °C |