Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LC1500 IDEMITSU JAPAN
TARFLON™
Optical level
High mobility,transparent,Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 15 kJ/m² |
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 50 |
| R 计秤 | ISO 2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 80 % | |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 65.0 Mpa |
| optical performance | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| transmissivity | ISO 13468-1 | 90.0 % | |
| ISO 9660 | >PC< | ||
| refractive index | ASTM D542 | 1.585 |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 2.00 mm | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.23 % |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 65.0 cm3/10min |
| Shrinkage rate | 流量 : 2.00 mm | 内部方法 | 0.50 - 0.70 % |
| density | ISO 1183 | 1.20 g/cm³ |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 127 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| RTI | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C |
| injection | Test Condition | Test Method | IDEMITSU JAPAN/LC1500 |
|---|---|---|---|
| drying time | 5.0 to 8.0 hr | ||
| Temperature in the middle of the barrel | 240 to 260 °C | ||
| Temperature at the rear of the barrel | 240 to 260 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 240 to 260 °C | ||
| Temperature | 80 to 120 °C |