Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 6013 S04 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6013 S04 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 1.8 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 2900 Mpa |
| elongation at break | 23°C | ISO 527-2 | 2.7 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 15 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 63 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6013 S04 |
|---|---|---|---|
| dielectric constant | 23°C | IEC 60250 | 2.35 1kHz |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm |
| optical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6013 S04 |
|---|---|---|---|
| refractive index | ISO 489 | 1.53 °C | |
| transmittance | 2000μm | ISO 13468-2 | 91 % |
| Flame retardant performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6013 S04 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/6013 S04 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.01 % |
| melt mass-flow rate | 260℃/2.16Kg | ISO 1133 | 14 cm3/10min |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6013 S04 |
|---|---|---|---|
| vicat | ISO 306/B50 | 137 °C | |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 130 °C |
| vicat | 玻璃转化温度 | ISO 11357-2 | 138 °C |