Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT HR5315 DUPONT USA
Cristin®
Electronic and electrical
Hydrolysis resistance、Glass fiber reinforced、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HR5315 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 40 kJ/m² |
| -40°C | ISO 180/1U | 30 kJ/m² | |
| 23°C | ISO 180/1U | 45 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| -30°C | ISO 179/1eU | 30 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT USA/HR5315 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 115 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/HR5315 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5200 Mpa | |
| Tensile strain | 23℃，断裂 | ISO 527-1 | 3 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 5000 Mpa |
| bending strength | 23℃ | ISO 178 | 140 MPa |
| Tensile modulus | 23℃ | ISO 527-1 | 5200 MPa |
| bending strength | ISO 178 | 150 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | ISO 178 | 4700 Mpa | |
| 23℃ | ISO 178 | 4500 MPa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 4200 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 95.0 Mpa |
| Suspended wall beam without notch impact strength | 23 ℃, Type 1 | ISO 180 | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HR5315 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| dielectric strength | IEC 60243-1 | 42 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010 |
| relative permittivity | 1MHz | IEC 60250 | 3.60 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| flammability | Test Condition | Test Method | DUPONT USA/HR5315 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/HR5315 |
|---|---|---|---|
| FlowLength2 | 2.00mm，FlowLength | 430 mm | |
| Shrinkage rate | Flow | ISO 294-4 | 0.5 % |
| TD | ISO 294-4 | 1.1 % | |
| MD | ISO 294-4 | 0.50 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.40 % |
| viscosity number | ISO 307 | 95.0 cm³/g | |
| MediumDensity | 1.14 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| Shrinkage rate | Across Flow | ISO 294-4 | 1.1 % |
| SpecificHeatCapacity of Melt | 1860 J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/HR5315 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| ISO 3146 | 225 ℃ | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.1E-05 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 65.0 °C |