PC RY2200 IDEMITSU JAPAN
TARFLON™
Automotive Applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| ISO Shortcut | >PC< |
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| M计秤 | ISO 2039-2 | 50 |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| Nominal tensile fracture strain | ISO 527-2 | 95 % | |
| bending strength | ISO 178 | 90.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 80 kJ/m² | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 65.0 Mpa |
| Rockwell hardness | M 计秤 | ISO 2039-2 | 50 |
| elongation at break | ISO 527-2 | 95 % |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| dielectric constant | 1MHz | IEC 60250 | 2.85 |
| 1 MHz | IEC 60250 | 2.85 | |
| arc resistance | ASTM D495 | 110 sec |
| optical performance | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| transmissivity | ISO 13468-1 | 85.0to89.0 % |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| Melt volume flow rate | MVR | ISO 1133 | 12 cm3/10min |
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.50-0.70 % |
| MD: 2.00 mm | 内部方法 | 0.5-0.7 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 12.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.23 % |
| Shrinkage rate | TD | 内部方法 | 0.5-0.7 % |
| MD:2.00mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 平衡,23℃, 50% RH | ISO 62 | 0.23 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/RY2200 |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.000065 cm/cm/℃ | |
| UL flame retardant rating | 3.00 mm | UL 94 | V-0 |
| RTI Imp | 1.5mm | UL 746 | 125 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 125 °C |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 125 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |