PC FPR4500 BK MITSUBISHI ENGINEERING JAPAN
IUPILON™
Automotive sector
Flame retardant,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FPR4500 BK |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 4.E+15 Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 3.1 | |
| Volume resistivity | ASTM D257/IEC 60093 | 2.E+14 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FPR4500 BK |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 97 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2700 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 2600 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 72 % |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FPR4500 BK |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.3 - 0.5 % | |
| density | ASTM D792/ISO 1183 | 1.19 |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FPR4500 BK |
|---|---|---|---|
| process temperature | 240-290 °C | ||
| Dry conditions | 热风干燥 80-90℃---約4-8小时 | ||
| screw speed | 50-150 rpm | ||
| Temperature | 60-90 °C |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FPR4500 BK |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0(0.8mm) |