PA6 SCANAMID 6 B43^D F15 POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B43^D F15 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | kJ/m² | 18 22 |
| -20°C | kJ/m² | 14 -- |
| hardness | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B43^D F15 |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | 73 -- |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B43^D F15 |
|---|---|---|---|
| Flexural modulus | 23°C | MPa | 4200 2800 |
| tensile strength | MPa | 115 65.0 | |
| Tensile strain | 断裂 | % | 6.5 9.5 |
| bending strength | MPa | 160 90.0 |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B43^D F15 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | HB -- | |
| Hot filament ignition temperature | 2.0mm | °C | 650 -- |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B43^D F15 |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.40 -- |
| density | g/cm³ | 1.18 -- | |
| Shrinkage rate | TD | % | 0.90 -- |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B43^D F15 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 205 -- |
| 1.8MPa,未退火，HDT | °C | 170 -- | |
| vicat | °C | >200 -- |