PBT 1200M TORAY JAPAN
Toraycon®
Bottle cap、Electric wire、Cable、Food service sector
transparent、standard
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| Melting temperature | 224 °C | ||
| Flame retardancy | UL94 HB |
| Mechanical Properties | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| Tensile Stress | ISO527-2 | 58.0 Mpa | |
| Flexural Strength | ASTM D790/ISO 178 | 83 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 120 % | |
| Tensile Elongation | 断裂 | ASTMD638 | >150 % |
| Flexural Modulus | ASTMD790 | 2500 Mpa | |
| Tensile Strength | ASTM D638/ISO 527 | 58 kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTMD790 | 82.0 Mpa | |
| Charpy impact strength | ASTM D256/ISO 179 | 5.1 kg·cm/cm(J/M)ft·lb/in | |
| Tensile Strength | 屈服 | ASTMD638 | 54.0 Mpa |
| Flexural Modulus | ISO178 | 2400 Mpa | |
| Flexural Strength | ISO 178 | 83 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 5.1 KJ/m | |
| Tensile Strain | 断裂 | ISO527-2 | 120 % |
| Flexural Stress | ISO178 | 83.0 Mpa | |
| Flexural Modulus | ISO 178 | 2.4 Gpa | |
| ASTM D790/ISO 178 | 2.4 kg/cm²(MPa)[Lb/in²] | ||
| Tensile Strength | ISO 527-1/-2 | 58 MPa |
| Physical | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 16.0 cm3/10min |
| Melt Mass-Flow Rate | 250°C/1.0kg | ISO1133 | 8.7 g/10min |
| parent Viscosity | 0.5%OCP | 内部方法 | 1.23 cm³/g |
| Physical Properties | Test Condition | Test Method | TORAY JAPAN/1200M |
|---|---|---|---|
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 224 g/10min | |
| Density | ASTM D792/ISO 1183 | 1.315 |