PA6 TP-4407 ZIG SHENG TAIWAN
ZISAMIDE®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ZIG SHENG TAIWAN/TP-4407 |
|---|---|---|---|
| melt mass-flow rate | 98 g/min | ||
| melting temperature | 224 °C | ||
| relative viscosity | 96%H2SO4,25℃ | 2.70±0.05 |
| Mechanical properties | Test Condition | Test Method | ZIG SHENG TAIWAN/TP-4407 |
|---|---|---|---|
| Fracture radius | 498 Kgf/cm | ||
| bending strength | ASTM D790/ISO 178 | 956 kg/cm²(MPa)[Lb/in²] | |
| elongation | 5.3 % | ||
| Flexural modulus | ASTM D790/ISO 178 | 22700 kg/cm²(MPa)[Lb/in²] | |
| Bending radius | 956 Kgf/cm | ||
| elongation | ASTM D638/ISO 527 | 5.3 % | |
| elongation at break | ASTM D638/ISO 527 | 307 % | |
| tensile strength | ASTM D638/ISO 527 | 547 kg/cm²(MPa)[Lb/in²] | |
| 547 Kgf/cm | |||
| Flexural modulus | 22700 Kgf/cm | ||
| elongation | 断裂 | 307 % |
| Physical properties | Test Condition | Test Method | ZIG SHENG TAIWAN/TP-4407 |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 98 g/10min |
| Thermal performance | Test Condition | Test Method | ZIG SHENG TAIWAN/TP-4407 |
|---|---|---|---|
| melting temperature | 224 ℃（℉） |