MVLDPE FPS117-C NOVA CANADA
SURPASS®
film、Laminate、film
antioxidant、Good sealing performance、High toughness、Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | NOVA CANADA/FPS117-C |
|---|---|---|---|
| LowFrictionPuncture-BlownFilm | 25.0µm | 内部方法 | 790 J/cm |
| film | Test Condition | Test Method | NOVA CANADA/FPS117-C |
|---|---|---|---|
| Film thickness - tested | 25 µm | ||
| tensile strength | Break,25µm,BlownFilm | ASTMD882 | 42.0 Mpa |
| Tensile strain | Break,25µm,BlownFilm | ASTMD882 | 760 % |
| tensile strength | Yield,25µm,BlownFilm | ASTMD882 | 9.00 Mpa |
| Seal Initiation Temperature | 25µm,BlownFilm | 100 °C | |
| Tensile strain MD | Break,25µm,BlownFilm | ASTMD882 | 540 % |
| ElmendorfTearStrength-MD | 25µm,BlownFilm | ASTMD1922 | 300 g |
| Secant modulus -1% Decant, MD | 25µm,BlownFilm | ASTMD882 | 126 Mpa |
| ElmendorfTearStrength-TD | 25µm,BlownFilm | ASTMD1922 | 450 g |
| Secant modulus -1% Decant, TD | 25µm,BlownFilm | ASTMD882 | 132 Mpa |
| Falling hammer impact | 25µm,吹塑薄膜 | ASTMD1709A | 400 g |
| optical performance | Test Condition | Test Method | NOVA CANADA/FPS117-C |
|---|---|---|---|
| gloss | 45°,25.0µm,BlownFilm2 | ASTMD2457 | 72 |
| 45°,25.0µm,BlownFilm3 | ASTMD2457 | 37 | |
| Haze ratio | 25.0µm,BlownFilm2 | ASTMD1003 | 7.0 % |
| 25.0µm,BlownFilm3 | ASTMD1003 | 16 % |
| physical property | Test Condition | Test Method | NOVA CANADA/FPS117-C |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 1.0 g/10min |