Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PES A G/30 LATI ITALY
LAPEX
--
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLATI ITALY/A G/30
Impact strength of simply supported beam without notch23°CISO 179/1eU25 kJ/m²
Supplementary InformationTest ConditionTest MethodLATI ITALY/A G/30
dimensional stability74.0
Mechanical propertiesTest ConditionTest MethodLATI ITALY/A G/30
Tensile modulus60°CISO 527-2/19400 Mpa
Tensile strain断裂,23°CISO 527-2/52.0 %
tensile strength 断裂,23°CISO 527-2/5130 Mpa
Tensile modulus90°CISO 527-2/19200 Mpa
23°CISO 527-2/19600 Mpa
Tensile strain断裂,120°CISO 527-2/52.4 %
Tensile modulus150°CISO 527-2/18600 Mpa
120°CISO 527-2/19000 Mpa
Tensile strain断裂,150°CISO 527-2/52.5 %
tensile strength 断裂,90°CISO 527-2/5115 Mpa
断裂,120°CISO 527-2/5100 Mpa
断裂,150°CISO 527-2/590.0 Mpa
Tensile strain断裂,60°CISO 527-2/52.1 %
断裂,90°CISO 527-2/52.3 %
tensile strength 断裂,60°CISO 527-2/5125 Mpa
flammabilityTest ConditionTest MethodLATI ITALY/A G/30
UL flame retardant rating3.0mmUL 94V-0
1.5mmUL 94V-0
Limiting Oxygen IndexASTM D286340 %
physical property Test ConditionTest MethodLATI ITALY/A G/30
Shrinkage rateMD:2.00mmISO 294-40.30-0.45 %
Water absorption rate23°C,24hrISO 620.17 %
Shrinkage rateTD:2.00mmISO 294-40.50-0.70 %
Thermal performanceTest ConditionTest MethodLATI ITALY/A G/30
Heat distortion temperature连续使用温度3，HDT185 °C
0.45MPa,未退火，HDTISO 75-2/B220 °C
vicatISO 306/B50220 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A215 °C
Linear coefficient of thermal expansionMD：30到100°CISO 11359-24E-06 cm/cm/°C