Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3EG7 BASF GERMANY
Ultramid®
Mechanical components,Electrical components,Shell,Automotive sector,container
Dimensional stability,Oil resistant,High rigidity,Filler: Glass fiber reinf,35% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/A3EG7 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 11.143to19.964 |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 3.065to3.343 |
| hardness | Test Condition | Test Method | BASF GERMANY/A3EG7 |
|---|---|---|---|
| ball-indentation hardness | 222.76to370.34 MPa |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3EG7 |
|---|---|---|---|
| Tensile strain | 断裂,23℃ | % | 1.9to3.1 |
| tensile strength | 断裂,23℃ | 144.83to292.41 MPa | |
| Tensile modulus | 23℃ | 8206.9to28000.0 MPa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/A3EG7 |
|---|---|---|---|
| dielectric strength | 23℃ | V/mil | 840 |
| Volume resistivity | 23℃ | ohms·cm | 1.0E+12-1.0E+14 |
| physical property | Test Condition | Test Method | BASF GERMANY/A3EG7 |
|---|---|---|---|
| Balance, 23 ℃, 50% RH | % | 1.2to1.5 | |
| density | 23℃ | g/cm³ | 1.28-1.85 |
| Saturation, 23 ℃ | % | 3.5to5.0 | |
| Shrinkage rate | 23℃ | % | 0.10-0.31 |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/A3EG7 |
|---|---|---|---|
| 8.0Mpa, Not annealed | °C | 65to220 | |
| Continuous use temperature | °C | 110to220 | |
| flow | mm/mm/°C | 142.2E-5-203.2E-5 | |
| 1.8MPa, Not annealed | °C | 230to250 | |
| horizontal | mm/mm/°C | 68.6E-5-127.0E-5 | |
| melting temperature | °C | 260 |