Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC L-1225L TEIJIN JAPAN
PANLITE®
Electrical appliances、Electrical field、Electronic field
High mobility、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 °C |
| RTIElec | 1.5mm | UL746 | 125 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 139 °C |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 146 ℃（℉） | |
| RTIStr | 1.5mm | UL746 | 125 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 126 °C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | ISO306/B50 | 146 °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 18.0 cm3/10min |
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 % |
| MD:4.00mm | 内部方法 | 0.50to0.70 % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.20 % |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2350 Mpa | |
| Flexural Strength | ASTM D790/ISO 178 | 93 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | >50 % | |
| Tensile Stress | 屈服 | ISO527-2/50 | 61.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 % |
| Tensile Modulus | ISO527-2/1 | 2400 Mpa | |
| Nominal Tensile Strain at Break | ISO527-2/50 | >50 % | |
| Flexural Stress | ISO178 | 93.0 Mpa | |
| Tensile Modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | 6 % | |
| Flexural Modulus | ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] |
| Optical | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.585 | |
| ASTM D542/ISO 489 | 1.585 | ||
| Transmittance | ASTM D1003/ISO 13468 | 88 % | |
| 3000µm | ASTMD1003 | 88.0 % |
| Impact Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | NoBreak |
| Physical Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.2 % | |
| Modeling Shrinkage | ASTM D955 | 0.5~0.7 % |
| Flammability | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Flame Rating | 0.40mm | UL94 | V-2 |
| 1.9mm | UL94 | HB | |
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 850 °C |
| Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 850 °C |
| 3.0mm | IEC60695-2-12 | 960 °C | |
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 875 °C |
| Electrical Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225L |
|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 30 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 250 V | |
| Surface Resistivity | ASTM D257/IEC 60093 | >1×1015 Ω | |
| Dielectric Constant | ASTM D150/IEC 60250 | 3.1 | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 3.00 |
| Arc Resistance | ASTM D495/IEC 60112 | 30 | |
| Volume Resistivity | ASTM D257/IEC 60093 | >1×1013 Ω.cm | |
| Relative Permittivity | 100Hz | IEC60250 | 3.10 |
| Dissipation Factor? | 1MHz | IEC60250 | 9E-03 |
| 100Hz | IEC60250 | 1E-03 |