PC/PET X5630Q SABIC INNOVATIVE US
XYLEX™ 
Automotive Applications
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/X5630Q
Heat Deflection Temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距ISO 75-2/Af108 °C
Vicat Softening Temperature--ISO 306/B50137 °C
ISO 306/B120140 °C
Linear thermal expansion coefficient横向 : -30 到 80°CISO 11359-21.0E-4 cm/cm/°C
流动 : -30 到 80°C3.8E-5 cm/cm/°C
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/X5630Q
Middle Temperature250 到 270 °C
Drying Time4.0 到 6.0 hr
Suggested Shot Size50 到 80 %
Drying Temperature110 °C
Mold Temperature65 到 90 °C
Vent Depth0.013 到 0.020 mm
Suggested Max Moisture0.020 %
Processing (Melt) Temp260 到 275 °C
Rear Temperature245 到 265 °C
Nozzle Temperature255 到 270 °C
Front Temperature255 到 275 °C
Back Pressure0.300 到 0.700 Mpa
Screw Speed50 到 80 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/X5630Q
Moisture Absorption平衡, 23°C, 50% RHISO 620.14 %
Melt Mass-Flow Rate265°C/5.0 kgASTM D123820 g/10 min
Melt Volume flow RateISO 113317.0 cm3/10min
Modeling Shrinkage - Flow内部方法0.50 到 0.70 %
Moisture Absorption饱和, 23°CISO 620.42 %
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/X5630Q
Tensile Stress屈服ISO 527-2/553.0 Mpa
断裂41.0 Mpa
Tensile Strain14 %
屈服3.3 %
Tensile ModulusISO 527-2/14340 Mpa
Flexural ModulusISO 1784110 Mpa
Flexural Stress92.0 Mpa
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/X5630Q
Unnotched Izod Impact Strength23°CISO 180/1U120 kJ/m²
Notched Izod Impact StrengthISO 180/1A6.0 kJ/m²
-30°C4.0 kJ/m²
Unnotched Izod Impact StrengthISO 180/1U80 kJ/m²