PBT LONGLITE® PBT 3015-200S Chang Chun Plastics Co., Ltd. (CCP Group)
--
--
Filler, glass fiber reinforced material, 15%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3015-200S |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3015-200S |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3400 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.5 % |
| Tensile modulus | 23°C | ISO 527-2 | 4200 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 75.0 MPa |
| bending strength | 23°C | ISO 178 | 115 MPa |
| Electrical performance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3015-200S |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 22 kV/mm |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| flammability | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3015-200S |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3015-200S |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 25 g/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.1to1.4 % |
| MD | ISO 294-4 | 0.30to0.60 % | |
| density | ISO 1183 | 1.36 g/cm³ |
| Thermal performance | Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 3015-200S |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 185 °C |