EHMWPE Quadrant EPP CESTILENE HD 1000 R Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 1000 R | |
|---|---|---|---|
| compression stress | 1%应变 | ISO 604/1 | 6.00 MPa |
| Nominal tensile fracture strain | ISO 527-2/1B/50 | >50 % | |
| Tensile modulus | ISO 527-2/1B/1 | 950 MPa | |
| Linear coefficient of thermal expansion | MD：23到100°C | 2E-04 cm/cm/°C | |
| ball-indentation hardness | ISO 2039-1 | 38.0 MPa | |
| melting temperature | ISO 11357-3 | 130to135 °C | |
| density | ISO 1183 | 0.930 g/cm³ | |
| Shore hardness | 邵氏D,15秒 | ISO 868 | 61 |
| vicat | ISO 306/B | 80.0 °C | |
| molecular weight distribution | 4000000 g/mol | ||
| Shore hardness | 邵氏D,3秒 | ISO 868 | 63 |
| Minimum operating temperature | -150 °C | ||
| Relative Weight Loss | --6 | 内部方法 | 150 |
| --5 | 内部方法 | 180 | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| tensile strength | 屈服 | ISO 527-2/1B/50 | 22.0 MPa |
| compression stress | 2%应变 | ISO 604/1 | 10.5 MPa |
| Continuous use temperature | --3 | 80.0 °C | |
| thermal conductivity | 23°C | 0.40 W/m/K | |
| Charpy Notched Impact Strength | --2 | 内部方法 | >80 kJ/m² |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| Continuous use temperature | --4 | 120 °C | |
| Charpy Notched Impact Strength | 局部断裂 | ISO 179/1eA | >90 kJ/m² |
| compression stress | 5%应变 | ISO 604/1 | 18.0 MPa |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 42.0 °C |
| Tensile strain | 屈服 | ISO 527-2/1B/50 | 13 % |
| Limiting Oxygen Index | ISO 4589-2 | <20 % | |
| Water absorption rate | 饱和,23°C,1.00mm | ISO 62 | 0.020 % |