PA66 AKV30 GIT H2.0 LANXESS GERMANY
Durethan® 
--
Filler: Glass fiber reinf,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
Ball Pressure TestISO 2039-1230 Mpa
Supplementary InformationTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
ISO ShortcutISO 1874PA66.GR.14-110.GF30
thermal performanceTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
Hot deformation temperature8.0MPa,UnannealedISO 75-2/C135 °C
0.45MPa,UnannealedISO 75-2/B250 °C
1.8MPa,UnannealedISO 75-2/A250 °C
Linear coefficient of thermal expansionMD：23to55°CISO 11359-22.5E-05 cm/cm/°C
TD：23to55°CISO 11359-21E-04 cm/cm/°C
Melting temperatureISO 11357-3263 °C
Vicat softening temperatureISO 306/B120>230 °C
mechanical propertiesTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
Bending modulus23°CISO 178/A8400 Mpa
23°CASTM D790841 Mpa
bending strengthFlexuralStrainatFlexuralStrength5(23°C)4.0 %
23°CASTM D790290 Mpa
23°CISO 178290 Mpa
3.5%StrainISO 178/A-- Mpa
elongationBreak,23°CASTM D6383.0 %
Tensile modulus23°CASTM D63810300 Mpa
23°CISO 527-2/110600 Mpa
Tensile strainBreak,23°CISO 527-2/53.0 %
tensile strengthBreak,23°CISO 527-2/5185 Mpa
Break,23°CASTM D638179 Mpa
Electrical performanceTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
Compared to the anti leakage trace indexSolutionAIEC 60112 V
Dielectric strength23°C,1.00mmIEC 60243-140 KV/mm
Dissipation factor23°C,100HzIEC 602509E-03
23°C,1MHzIEC 602500.018
Relative permittivity23°C,1MHzIEC 602504.00
23°C,100HzIEC 602504.00
Surface resistivityIEC 600931E+14 ohms
Volume resistivity23°CIEC 600931E+15 ohms·cm
Physical propertiesTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
Apparent densityISO 600.70 g/cm³
Shrinkage rateMD:280°C,3.00mm2ISO 25770.35 %
MD:120°C,2hr,3.00mm3ISO 25770.040 %
TD:280°C,3.00mm2ISO 25771.5 %
TD:120°C,2hr,3.00mm3ISO 294-40.050 %
Water absorption rateEquilibrium,23°C,50%RHISO 622.0 %
Saturation,23°CISO 625.5 %
impact performanceTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
Impact strength of simply supported beam without notch-30°CISO 179/1eU70 kJ/m²
23°CISO 179/1eU90 kJ/m²
flammabilityTest ConditionTest MethodLANXESS GERMANY/AKV30 GIT H2.0
Burning wire flammability index2.0mmIEC 60695-2-12600 °C
Extreme Oxygen IndexISO 4589-223 %
UL flame retardant rating3.2mmUL 94HB
1.6mmUL 94HB