PBT 1184G-30 TORAY JAPAN
Toraycon®
Automotive Applications
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1184G-30 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 61 kg·cm/cm(J/M)ft·lb/in | |
bending strength | ASTM D790/ISO 178 | 215 kg/cm²(MPa)[Lb/in²] | |
Flexural modulus | ASTM D790/ISO 178 | 9400 kg/cm²(MPa)[Lb/in²] | |
Rockwell hardness | ASTM D785 | 87 M | |
bending strength | ASTM D790 | 215 Mpa | |
elongation | ASTM D638 | 4 % | |
elongation at break | ASTM D638/ISO 527 | 4 % | |
Rockwell hardness | ASTM D785 | M87 | |
tensile strength | ASTM D638/ISO 527 | 145 kg/cm²(MPa)[Lb/in²] | |
coefficient of friction | 对本身 | ASTM D1894 | 0.20 |
Flexural modulus | ASTM D790 | 9.4 GPa | |
Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 62 J/m |
tensile strength | 23℃ | ASTM D638 | 145 Mpa |
coefficient of friction | 对金属 | ASTM D1894 | 0.15 |
Electrical performance | Test Condition | Test Method | TORAY JAPAN/1184G-30 |
---|---|---|---|
dielectric constant | 50Hz | ASTM D150 | 4.0 |
Dielectric loss | 10,正切 | ASTM D150 | 0.01 |
dielectric strength | ASTM D149 | 27 MV/m | |
dielectric constant | ASTM D150/IEC 60250 | 3.8 | |
10 | ASTM D150 | 3.8 | |
Dielectric loss | 50Hz,正切 | ASTM D150 | 0.001 |
Volume resistivity | ASTM D257/IEC 60093 | 2.5x10^14 Ω.cm | |
ASTM D257 | 2.5 | ||
arc resistance | ASTM D495 | 123 sec |
other | Test Condition | Test Method | TORAY JAPAN/1184G-30 |
---|---|---|---|
characteristic | 增强阻燃等级.V-0.30%玻纤增强 |
Physical properties | Test Condition | Test Method | TORAY JAPAN/1184G-30 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.65 | |
Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
physical property | Test Condition | Test Method | TORAY JAPAN/1184G-30 |
---|---|---|---|
Water absorption rate | 23℃,65%RH 24H | ASTM D570 | 0.07 % |
Thermal performance | Test Condition | Test Method | TORAY JAPAN/1184G-30 |
---|---|---|---|
Combustibility (rate) | UL 94 | V-0 | |
Heat distortion temperature | HDT | ASTM D648/ISO 75 | 210 ℃(℉) |
0.45Mpa,HDT | ASTM D648 | 223 °C | |
1.82Mpa,HDT | ASTM D648 | 210 °C | |
Linear coefficient of thermal expansion | ASTM D696 | 4.1 | |
ASTM D696/ISO 11359 | 4.1x10^-5 mm/mm.℃ | ||
UL flame retardant rating | UL 94 | V-0 |