PA66 80G14AHS-BK099 DUPONT USA
Zytel®
Electrical applications,small home appliances
High impact resistance,Thermal stability,Filler: Glass fiber reinf,14% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DUPONT USA/80G14AHS-BK099 |
|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 3.90 µgC/g | |
| Odor | VDA270 | 4.50 |
| thermal performance | Test Condition | Test Method | DUPONT USA/80G14AHS-BK099 |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO 75-2/B | 258 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 240 °C | |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 9.7E-05 cm/cm/°C |
| MD：-- | ISO 11359-2 | 4E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 4E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 4E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1E-04 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.4E-04 cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 263 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/80G14AHS-BK099 |
|---|---|---|---|
| Bending modulus | ISO 178 | 4400 Mpa | |
| Tensile modulus | ISO 527-2 | 5000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.8 % |
| tensile strength | 断裂 | ISO 527-2 | 110 Mpa |
| Physical properties | Test Condition | Test Method | DUPONT USA/80G14AHS-BK099 |
|---|---|---|---|
| density | ISO 1183 | 1.19 g/cm³ | |
| Shrinkage rate | MD | ISO 294-4 | 0.70 % |
| TD | ISO 294-4 | 0.90 % | |
| Top out temperature | 210 °C |
| impact performance | Test Condition | Test Method | DUPONT USA/80G14AHS-BK099 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 6.0 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| flammability | Test Condition | Test Method | DUPONT USA/80G14AHS-BK099 |
|---|---|---|---|
| Burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| Extreme Oxygen Index | ISO 4589-2 | 21 % | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | UL 94 | HB |