MVLDPE 5500G STYRON US
DOWLEX™
film
Heat sealing performance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| Secant modulus | 2%正割,TD | ASTM D882 | 165 Mpa |
| film strength | MD | ASTM D882 | 82.7 J/cm³ |
| Thin film puncture strength | 内部方法 | 5.65 J | |
| Secant modulus | 1%正割,TD | ASTM D882 | 193 Mpa |
| tensile strength | MD:屈服 | ASTM D882 | 18.3 Mpa |
| elongation | MD:断裂 | ASTM D882 | 400 % |
| Dart impact | ASTM D1709A | 650 g | |
| Thin film puncture strength | 内部方法 | 29.0 J/cm³ | |
| tensile strength | TD:屈服 | ASTM D882 | 10.3 Mpa |
| Thin film puncture strength | 内部方法 | 62.3 N | |
| Elmendorf tear strength | MD | ASTM D1922 | 350 g |
| tensile strength | MD:断裂 | ASTM D882 | 41.4 Mpa |
| film thickness | 25 µm | ||
| tensile strength | TD:断裂 | ASTM D882 | 37.9 Mpa |
| Secant modulus | 2%正割,MD | ASTM D882 | 141 Mpa |
| Elmendorf tear strength | TD | ASTM D1922 | 600 g |
| film strength | TD | ASTM D882 | 91.0 J/cm³ |
| Secant modulus | 1%正割,MD | ASTM D882 | 162 Mpa |
| elongation | TD:断裂 | ASTM D882 | 500 % |
| optical performance | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 45 |
| Haze ratio | ASTM D1003 | 12 % |
| physical property | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.5 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| vicat | ASTM D1525 | 97.0 °C | |
| melting temperature | 内部方法 | 122 °C |