LCP T130 CELANESE USA
VECTRA® 
Automotive Applications,Home appliance components
heat-resisting,enhance,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Basic PerformanceTest ConditionTest MethodCELANESE USA/T130
densityISO 11831400 kg/m
Water absorption rate23℃/50rhISO 620.030 %
thermal performanceTest ConditionTest MethodCELANESE USA/T130
CombustibilityUL 94V-0
Hot deformation temperature1.80MPaISO 75-1187 °C
8.00MPaISO 75-1145 °C
Linear coefficient of thermal expansionnormalISO 11359-10.000038 cm/cm℃
parallelISO 11359-14E-06 cm/cm℃
Vicat softening temperature50℃/h 50NISO 306145 °C
mechanical propertiesTest ConditionTest MethodCELANESE USA/T130
Bending modulus23℃ISO 1789100 Mpa
bending strength23℃ISO 178158 Mpa
Charpy Notched Impact Strength23℃ISO 179/1eA95.0 KJ/m
elongationBreakISO 527-13.4 %
Impact strength of cantilever beam gap23℃ISO 180/1A95.0 KJ/m
Impact strength of simply supported beam without notch23℃ISO 179/1eU267 KJ/m
-30℃ISO 179/1eU53.0 KJ/m
Suspended wall beam without notch impact strength23℃ISO 180/1U252 KJ/m
Tensile creep modulus1hrISO 899-19000 Mpa
1000hrISO 899-16600 Mpa
Tensile modulusISO 527-110600 Mpa
tensile strengthISO 527-1182 Mpa
Electrical performanceTest ConditionTest MethodCELANESE USA/T130
Compared to the Leakage Traceability Index (CTI)IEC 60112150
Dielectric loss100HzIEC 602500.016
1000HzIEC 602500.020
Dielectric strengthIEC 60243-147 KV/mm
Relative permittivity100HzIEC 602503.20
1000HzIEC 602503.00
Surface resistivityIEC 600931E+14 ohms
Volume resistivityIEC 600931E+13 ohm.m
Physical propertiesTest ConditionTest MethodCELANESE USA/T130
Shrinkage rateparallelISO 25770.70 %
normalISO 25770.0 %