PC EFR3000-9001 MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Non specific food
High mobility,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000-9001
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000-9001
Tensile modulusISO 527-22300 Mpa
Nominal tensile fracture strainISO 527-267 %
bending strengthISO 17892.0 Mpa
Flexural modulusISO 1782500 Mpa
Tensile strain屈服ISO 527-24.7 %
tensile strength 屈服ISO 527-261.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000-9001
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
dielectric strength3.00mmIEC 60243-118 KV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600936E+15 ohms
Dissipation Factor1MHzIEC 602509E-03
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000-9001
UL flame retardant rating1.0mmUL 94V-0
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000-9001
Shrinkage rateTD:3.20mm0.50-0.70 %
Melt volume flow rate300°C/1.2kgISO 113321.0 cm3/10min
Shrinkage rate吸水率(饱和,23°C)0.24 %
MD:3.20mm0.50-0.70 %
melt mass-flow rate300°C/1.2kgISO 113322 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/EFR3000-9001
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B137 °C
1.8MPa,未退火,HDTISO 75-2/A125 °C
Linear coefficient of thermal expansionMDISO 11359-26.6E-05 cm/cm/°C
TDISO 11359-26.7E-05 cm/cm/°C