Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUX 2180T SABIC INNOVATIVE NANSHA
LEXAN™
Lighting applications
Optics,UV resistance,Aging resistance,Weather resistance,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX 2180T |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.70 |
| 50Hz | IEC 60250 | 2.70 | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.70 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| 60Hz | IEC 60250 | 1E-03 | |
| 1MHz | IEC 60250 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX 2180T |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| tensile strength | 断裂 | ISO 527-2/50 | 69.0 Mpa |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| tensile strength | 屈服 | ISO 527-2/50 | 62.0 Mpa |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| bending strength | ISO 178 | 90.0 Mpa | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 65 kJ/m² |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 10.0 mg |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 95.0 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX 2180T |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | <0.50 % |
| transmittance | 2540µm,420nm | 内部方法 | >88.0 % |
| 2540µm | ASTM D1003 | >90.0 % | |
| refractive index | ISO 489 | 1.586 | |
| transmittance | 5000µm | 内部方法 | >89.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX 2180T |
|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL 94 | V-2 |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | >875 °C |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 850 °C |
| Limiting Oxygen Index | ISO 4589-2 | 25 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX 2180T |
|---|---|---|---|
| Outdoor applicability | UL 746C | f1 | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 18.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| Shrinkage rate | MD1 | 内部方法 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX 2180T |
|---|---|---|---|
| -- | ISO 306/B50 | 140 °C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 133 °C | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 122 °C | |
| -- | ISO 306/B120 | 141 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI Imp | UL 746 | 125 °C | |
| RTI | UL 746 | 125 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | UL 746 | 130 °C |