PC SC-1100R LOTTE KOREA
INFINO®
Industrial applications、Electrical field、Electronic field、Automotive sector、Automotive interior parts、Automotive External Parts、Industrial components
currency、High temperature resistan、transparent、Flame retardant、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | LOTTE KOREA/SC-1100R |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| R 级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/SC-1100R |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 64.0 Mpa |
| 屈服3 | ASTM D638 | 62.8 Mpa | |
| elongation | 断裂3 | ASTM D638 | 110 % |
| bending strength | --4 | ASTM D790 | 90.2 Mpa |
| --5 | ISO 178 | 92.0 Mpa | |
| Tensile modulus | --3 | ASTM D638 | 2260 Mpa |
| -- | ISO 527-2/50 | 2300 Mpa | |
| elongation | 断裂 | ISO 527-2/50 | 110 % |
| Flexural modulus | --4 | ASTM D790 | 2260 Mpa |
| --5 | ISO 178 | 2300 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 62.8 Mpa |
| 断裂 | ISO 527-2/50 | 64.0 Mpa |
| flammability | Test Condition | Test Method | LOTTE KOREA/SC-1100R |
|---|---|---|---|
| UL flame retardant rating | 0.830mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | LOTTE KOREA/SC-1100R |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 3.20 mm | ASTM D955 | 0.50 - 0.70 % |
| 流量 : 2.00 mm | ISO 294-4 | 0.50 - 0.70 % | |
| 流动 : 3.20 mm | ASTM D955 | 0.50 - 0.70 % | |
| 横向流量 : 2.00 mm | ISO 294-4 | 0.50 - 0.70 % | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 12 g/10 min |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/SC-1100R |
|---|---|---|---|
| vicat | ISO 306/B50 | 146 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/A | 125 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 127 °C | |
| 0.45 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/B | 137 °C | |
| 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 137 °C |
| injection | Test Condition | Test Method | LOTTE KOREA/SC-1100R |
|---|---|---|---|
| screw speed | 30 to 50 rpm | ||
| Suggested maximum moisture content | 0.040 % | ||
| Vacuum dryer | 80 °C | ||
| Injection Pressure | 98.1 Mpa | ||
| Hot air dryer | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 260 to 270 °C | ||
| Temperature at the rear of the barrel | 100 to 260 °C | ||
| Vacuum dryer | 4.0 to 6.0 hr | ||
| Temperature at the front of the material cylinder | 260 to 280 °C | ||
| Back pressure | 0.981 to 1.96 Mpa | ||
| Temperature | 80 to 110 °C | ||
| Hot air dryer | 80 °C | ||
| Spray nozzle temperature | 280 °C |