PC TAROLON 3020 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTaro Plast S.p.A./TAROLON 3020
Charpy Notched Impact Strength23°CISO 17935 kJ/m²
Impact strength of cantilever beam gap23°C,3.20mmASTMD256750 J/m
Electrical performanceTest ConditionTest MethodTaro Plast S.p.A./TAROLON 3020
Volume resistivityASTM D257>1.0E+15 ohms·cm
dielectric strength2.00mmASTM D14920 kV/mm
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 3
Mechanical propertiesTest ConditionTest MethodTaro Plast S.p.A./TAROLON 3020
Flexural modulusASTMD7902500 MPa
elongation断裂ASTMD638100 %
bending strength屈服ASTM D79088.0 MPa
Tensile modulusASTMD6382300 MPa
tensile strength 屈服ASTMD63870.0 MPa
bending strength--3ISO 17888.0 MPa
flammabilityTest ConditionTest MethodTaro Plast S.p.A./TAROLON 3020
Hot filament ignition temperature2.0mmIEC 60695-2-13850 °C
UL flame retardant rating3.2mmUL 94V-2
1.6mmUL 94V-2
Limiting Oxygen IndexASTM D286326 %
physical property Test ConditionTest MethodTaro Plast S.p.A./TAROLON 3020
Shrinkage rateMDASTM D9550.50to0.70 %
Water absorption rate饱和ASTM D5700.35 %
densityASTMD7921.20 g/cm³
Water absorption rate23°C,24hrASTMD5700.12 %
melt mass-flow rate300°C/1.2kgASTMD123810 g/10min
Water absorption rate饱和,23°CISO 620.35 %
Shrinkage rateTDASTM D9550.50to0.70 %
Thermal performanceTest ConditionTest MethodTaro Plast S.p.A./TAROLON 3020
vicatISO 306/A50152 °C
Heat distortion temperature1.8MPa,未退火，HDTASTMD648140 °C
ball-indentation hardness125°CVDE0470通过
Linear coefficient of thermal expansionMD：-30到30°CASTM D6967E-05 cm/cm/°C