| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000M-7M2D109 |
|---|---|---|---|
| bending strength | 屈服23℃ | ASTM D790 | 93 Mpa |
| elongation | 23℃ | ASTM D638 | 44 % |
| Impact strength of cantilever beam gap | -30℃ | ASTM D256 | 12 J/m |
| Flexural modulus | 23℃ | ASTM D790 | 2400 Mpa |
| elongation | 屈服23℃ 50mm/min | ASTM D638 | 4 % |
| tensile strength | 屈服23℃ | ASTM D638 | 60 Mpa |
| 23℃ 50mm/min | ASTM D638 | 46 Mpa | |
| Impact strength of cantilever beam gap | 23℃，-30℃ | ASTM D256 | 55 J/m |
| Dart impact | 55 |
| Flame retardant performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000M-7M2D109 |
|---|---|---|---|
| UL flame retardant rating | 3.00mm | UL 94 | V-0 |
| 2.50mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000M-7M2D109 |
|---|---|---|---|
| Water absorption rate | 23℃ 50RH | ISO 62 | 0.2 % |
| melt mass-flow rate | 260℃ 2.16kg | ASTM D1238 | 25 g/10min |
| Shrinkage rate | 垂直3.2mm | ASTM D995 | 0.7 % |
| Water absorption rate | 23℃饱和 | ISO 62 | 0.6 % |
| density | ASTM D792 | 1.2 g/cm³ | |
| Shrinkage rate | 流动3.2mm | ASTM D995 | 0.5 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000M-7M2D109 |
|---|---|---|---|
| Heat distortion temperature | 未退火1.8MPa，HDT | ASTM D648 | 80 °C |
| Vertical expansion coefficient | ASTM D696 | 0.000080 cm/cm/℃ | |
| vicat | ASTM DI525 | 98 °C | |
| 120℃/hr 50N | ISO 306 | 100 °C | |
| 50℃/hr 50N | ISO 306 | 98 °C |