POM JW-01 CF2001 JAPAN POLYPLASTIC
DURACON®
Power tool accessories、Automotive components、Home appliance components
Thermal stability、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/JW-01 CF2001 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO2039-2 | 80 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/JW-01 CF2001 |
|---|---|---|---|
| ColorNumber | CF2001 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/JW-01 CF2001 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 35 % | |
| Wear factor | 0.98MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec7 | JISK7218 | 220 10^-8mm³/N·m | |
| 0.98MPa,0.30m/sec5 | JISK7218 | 21 10^-8mm³/N·m | |
| 0.060MPa,0.15m/sec6 | JISK7218 | 80 10^-8mm³/N·m | |
| 与钢-动态3 | JISK7218 | 0.17 | |
| Tensile stress | ISO527-2 | 54.0 Mpa | |
| Dynamic2 | JISK7218 | 0.21 | |
| Bending stress | ISO178 | 79.0 Mpa | |
| Tensile modulus | ISO527-2 | 2600 Mpa | |
| Flexural modulus | ISO178 | 2400 Mpa |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/JW-01 CF2001 |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/JW-01 CF2001 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO294-4 | 1.9 % |
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 46 g/10min |
| Shrinkage rate | TD:2.00mm | ISO294-4 | 1.7 % |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 39.0 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO62 | 0.60 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/JW-01 CF2001 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/A | 98.0 °C | |
| MD：23到55°C | 内部方法 | 1.2E-04 cm/cm/°C | |
| TD：23to55°C | 内部方法 | 1.2E-04 cm/cm/°C |