PA66 103HSL NC010 DUPONT SINGAPORE
Zytel®
Automotive sector、Electronic field
Flame retardant、heat-resisting、Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| -30°C | ISO180/1U | 300kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.5 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 6.0 kJ/m² |
| 23°C | ISO180/1U | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 5.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.5 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 400kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 2.10 µgC/g | |
| Odor | VDA270 | 2.50 |
| film | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| Tensile strain MD | Yield | ISO527-3 | 4.5 % |
| Mechanical properties | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 20 % | |
| TensileCreepModule | 1hr | ISO899-1 | -- Mpa |
| Tensile stress | 屈服 | ISO527-2 | 85.0 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 4.5 % |
| Tensile modulus | ISO527-2 | 3100 Mpa | |
| Flexural modulus | ISO178 | 2800 Mpa | |
| Tensile creep modulus | 1000hr | ISO899-1 | -- Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| Dissipation Factor | 1MHz | IEC60250 | 0.017 |
| CTI | IEC60112 | 600 V | |
| 1MHz | IEC60250 | 3.50 | |
| Volume resistivity | IEC60093 | 1E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | UL746 | PLC 0 |
| dielectric strength | IEC60243-1 | 31 KV/mm | |
| 100Hz | IEC60250 | 3.80 | |
| Dissipation Factor | 100Hz | IEC60250 | 7.5E-03 |
| flammability | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-2 |
| 0.71mm | UL94 | V-2 | |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 0.71mm | IEC60695-11-10,-20 | V-2 |
| 1.5mm | IEC60695-11-10,-20 | V-2 | |
| Limiting Oxygen Index | ISO4589-2 | 28 % |
| physical property | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.3 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 8.5 % |
| viscosity number | ISO307 | 145 cm³/g | |
| MediumDensity | 0.980 g/cm³ | ||
| Ejection Temperature | 190 °C | ||
| Shrinkage rate | MD | ISO294-4 | 1.3 % |
| density | ISO1183 | 1.14 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 2.6 % |
| SpecificHeatCapacity of Melt | 2790 J/kg/°C | ||
| ThermalConductivityofMelt | 0.16 W/m/K |
| Thermal performance | Test Condition | Test Method | DUPONT SINGAPORE/103HSL NC010 |
|---|---|---|---|
| TD | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| EffectiveThermal Diffusivity | 5E-08 m²/s | ||
| vicat | ISO306/B50 | 240 °C | |
| 0.45MPa,未退火 | ISO75-2/B | 200 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 70.0 °C | |
| Glass transition temperature 2 | ISO11357-2 | 60.0 °C | |
| melting temperature | ISO11357-3 | 262 °C | |
| MD | ISO11359-2 | 1E-04 cm/cm/°C |