PA66 66 H2 G/30 LATI ITALY
LATAMID
--
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | LATI ITALY/66 H2 G/30 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 85 kJ/m² |
Supplementary Information | Test Condition | Test Method | LATI ITALY/66 H2 G/30 |
---|---|---|---|
dimensional stability | 45.0 |
Mechanical properties | Test Condition | Test Method | LATI ITALY/66 H2 G/30 |
---|---|---|---|
Tensile modulus | 60°C | ISO 527-2/1 | 8500 Mpa |
Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.2 % |
tensile strength | 断裂,23°C | ISO 527-2/5 | 175 Mpa |
Tensile modulus | 90°C | ISO 527-2/1 | 7400 Mpa |
23°C | ISO 527-2/1 | 9400 Mpa | |
Tensile strain | 断裂,120°C | ISO 527-2/5 | 6.0 % |
Tensile modulus | 150°C | ISO 527-2/1 | 4400 Mpa |
Tensile strain | 断裂,150°C | ISO 527-2/5 | 6.5 % |
Tensile modulus | 120°C | ISO 527-2/1 | 5500 Mpa |
tensile strength | 断裂,90°C | ISO 527-2/5 | 110 Mpa |
断裂,120°C | ISO 527-2/5 | 100 Mpa | |
断裂,150°C | ISO 527-2/5 | 85.0 Mpa | |
Tensile strain | 断裂,60°C | ISO 527-2/5 | 4.0 % |
断裂,90°C | ISO 527-2/5 | 5.5 % | |
tensile strength | 断裂,60°C | ISO 527-2/5 | 135 Mpa |
physical property | Test Condition | Test Method | LATI ITALY/66 H2 G/30 |
---|---|---|---|
Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.35-0.65 % |
Water absorption rate | 23°C,24hr | ISO 62 | 0.27 % |
Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.75-1.1 % |
Thermal performance | Test Condition | Test Method | LATI ITALY/66 H2 G/30 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 260 °C |
vicat | ISO 306/B50 | 255 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 245 °C |
Continuous use temperature | 130 °C | ||
Linear coefficient of thermal expansion | MD:30到100°C | ISO 11359-2 | 8E-06 cm/cm/°C |