Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM FG2015 KEP KOREA
KEPITAL®
--
Medium viscosity,Moderate heat resistance,High rigidity,Creep resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Basic performance | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| Shrinkage rate | flow,2.00MM | ASTM D955 | 0.80 % |
| density | ASTM D792 | 1.50 g/cm³ | |
| Water absorption rate | Equilibrium,23℃,60%rh | ASTM D570 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 175 kg/cm²(MPa)[Lb/in²] | |
| 23°C | ASTM D790 | 157 MPa | |
| Flexural modulus | ASTM D790/ISO 178 | 5200 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 7.0 kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 69.0 J/m |
| elongation at break | ASTM D638/ISO 527 | 3.6 % | |
| tensile strength | ASTM D638/ISO 527 | 120 kg/cm²(MPa)[Lb/in²] | |
| elongation | Break,23℃ | ASTM D638 | 3.0 % |
| Electrical performance | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1x10的16次方 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1x10的14次方 Ω.cm |
| other | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| characteristic | 中粘度.玻纤增强15%.一般注射成型 | ||
| Color | 本白色 | ||
| purpose | 适用于要求极高刚性的零部件.抗疲劳抗蠕变性和耐热性。 |
| Physical properties | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.8 % | |
| density | ASTM D792/ISO 1183 | 1.5 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 11.5 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| processability | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| process temperature | 180-210 °C | ||
| pressure | 500-1200kg/cm2（7.110-17.070psi） Mpa | ||
| Dry conditions | 80-100C（175-210F).3-4hrs | ||
| screw speed | 80-120转/分钟 rpm | ||
| Temperature | 60-80 °C |
| Thermal performance | Test Condition | Test Method | KEP KOREA/FG2015 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 164 °C |
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 164 ℃（℉） |
| melting temperature | 165 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 5 mm/mm.℃ |