Product Name
Brand Name
Usages
Properties
Certificates
LMDPE FF 506 Smooth-On, Inc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Smooth-On, Inc/FF 506 |
|---|---|---|---|
| elongation | TD:断裂,25µm,吹塑薄膜 | ISO 527-3 | 700 % |
| tensile strength | MD:屈服,25µm,吹塑薄膜 | ISO 527-3 | 16.0 MPa |
| TD:断裂,25µm,吹塑薄膜 | ISO 527-3 | 40.0 MPa | |
| Tensile modulus | 1%正割,TD:25µm,吹塑薄膜 | ISO 527-3 | 450 MPa |
| 1%正割,MD:25µm,吹塑薄膜 | ISO 527-3 | 400 MPa | |
| elongation | MD:断裂,25µm,吹塑薄膜 | ISO 527-3 | 550 % |
| Elmendorf tear strength | TD:25.0µm | ISO 6383-2 | 200.0 kN/m |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ISO 527-3 | 50.0 MPa |
| film thickness | 10to50µm | ||
| Elmendorf tear strength | MD:25.0µm | ISO 6383-2 | 40.0 kN/m |
| film thickness | 25 µm | ||
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ISO 527-3 | 18.0 MPa |
| Dart impact | 25µm,吹塑薄膜 | ISO 7765-1/A | 80 g |
| Mechanical properties | Test Condition | Test Method | Smooth-On, Inc/FF 506 |
|---|---|---|---|
| coefficient of friction | Dynamic,吹塑薄膜 | ISO 8295 | >0.50 |
| optical performance | Test Condition | Test Method | Smooth-On, Inc/FF 506 |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTM D2457 | 50 |
| Haze ratio | 25.0µm,吹塑薄膜 | ISO 14782 | 14 % |
| physical property | Test Condition | Test Method | Smooth-On, Inc/FF 506 |
|---|---|---|---|
| density | ISO 1183 | 0.934 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.75 g/10min |
| Thermal performance | Test Condition | Test Method | Smooth-On, Inc/FF 506 |
|---|---|---|---|
| melting temperature | 内部方法 | 128 °C | |
| brittle temperature | ASTM D746 | <-70.0 °C | |
| vicat | ISO 306/A | 118 °C |