Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV25F30 LANXESS GERMANY
Durethan®
Automotive components、Instrument components、Electronic and Electrical、Industrial applications、Communication equipment
Heat aging
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
| 23°C | ISO 180/1U | 50 kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 1.90 J |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 3.00 J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 1000 N |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 900 N |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6.GFHR.14-110.GF25 |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Volume resistivity | 23°C | IEC 60093 | 3.4E+14 ohms·cm |
| Surface Resistivity | IEC 60093 | 4.1E+13 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.3 % |
| Flexural modulus | 23°C | ISO 178/A | 10000 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 150 Mpa |
| Bending Strain | 23°C | ISO 178/A | 2.5 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 11000 Mpa |
| bending strength | 23°C | ISO 178/A | 230 Mpa |
| flammability | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| 0.8mm | IEC 60695-2-12 | 960 °C | |
| 0.40mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 775 °C |
| 0.40mm | IEC 60695-2-13 | 850 °C | |
| 0.8mm | IEC 60695-2-13 | 775 °C | |
| Burning Behavior | ISO 3795 | passed | |
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Shrinkage rate | MD:120°C,4小时,2.00mm3 | ISO 2577 | 0.10 % |
| TD:280°C,2.00mm2 | ISO 2577 | 0.60 % | |
| MD:280°C,2.00mm2 | ISO 2577 | 0.30 % | |
| TD:120°C,4小时,2.00mm3 | ISO 2577 | 0.10 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 222 °C | |
| vicat | ISO 306/B120 | 205 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |