Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

GPPS 147F BASF KOREA
Bycolene®
Transparent parts of refr、Household daily necessiti、chip、Monitor
Easy to process、Good heat resistance、Moderate liquidity、Universal type with good
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | BASF KOREA/147F |
---|---|---|---|
tensile elongation at break | 23℃ | ISO 527 | 3 % |
ball-indentation hardness | ISO 2039-1 | 150 Mpa | |
Tensile modulus | ISO 527 | 3300 Mpa | |
Melt volume flow rate | 200℃ / 5kg | ISO 1133 | 6.5 cm3/10min |
bending strength | ISO 178 | 98 Mpa | |
Impact strength of simply supported beam without notch | 23℃ | ISO 179 | 17 kJ/m² |
Charpy Notched Impact Strength | 23℃ | ISO 179 | 3 kJ/m² |
tensile yield strength | 23℃ | ISO 527 | 50 Mpa |
Electrical performance | Test Condition | Test Method | BASF KOREA/147F |
---|---|---|---|
dielectric constant | 100Hz | IEC 60250 | 2.5 - |
breakdown voltage | 短时,1.5 mm | IEC 60243-1 | 135 KV/mm |
Surface Resistivity | IEC 60093 | >1E14 Ohm | |
Volume resistivity | IEC 60093 | >1E16 ohm·m | |
dielectric constant | 1MHz | IEC 60250 | 2.5 - |
processability | Test Condition | Test Method | BASF KOREA/147F |
---|---|---|---|
Melting temperature range | ISO 294 | 180 - 260 ℃ | |
Mold temperature range | ISO 294 | 10 - 60 ℃ | |
Injection Speed | ISO 294 | 200 mm/s | |
Linear mold shrinkage rate | ISO 294-4 | 0.3 - 0.6 % |
physical property | Test Condition | Test Method | BASF KOREA/147F |
---|---|---|---|
Water absorption rate | 23℃, 50%RH 平衡 | ISO 62 | <0.1 % |
density | ISO 1183 | 1046 kg/m3 | |
Water absorption rate | 23℃ 饱和 | ISO 62 | <0.1 % |
Thermal performance | Test Condition | Test Method | BASF KOREA/147F |
---|---|---|---|
vicat | 10N, 50℃/h | ISO 306 | 100 ℃ |
Heat distortion temperature | 1.8MPa, 退火4h/80℃ | ISO 75 | 85 ℃ |
0.45MPa, 退火4h/80℃ | ISO 75 | 93 ℃ | |
vicat | 50N, 50℃/h | ISO 306 | 95 ℃ |