Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET XL1339U-BK1370 SABIC EU
XENOY™
Automotive components、Electronic and electrical
High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC EU/XL1339U-BK1370 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 45 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 35 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| -30°C | ISO 180/1U | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC EU/XL1339U-BK1370 |
|---|---|---|---|
| tensile strength | 屈服3 | ASTM D638 | 49.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 110 % |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 16.0 mg |
| elongation | 断裂 | ISO 527-2/50 | 70 % |
| Flexural modulus | --5 | ISO 178 | 2200 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 94.0 Mpa |
| --5,6 | ISO 178 | 80.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2090 Mpa |
| Poisson's ratio | ASTM E132 | 0.40 | |
| tensile strength | 断裂 | ISO 527-2/50 | 40.0 Mpa |
| Tensile modulus | ASTM D638 | 2090 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| 屈服3 | ASTM D638 | 5.0 % | |
| tensile strength | 断裂3 | ASTM D638 | 49.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC EU/XL1339U-BK1370 |
|---|---|---|---|
| dielectric strength | 3.20 mm, in Oil | ASTM D149 | 17 KV/mm |
| Volume resistivity | ASTM D257 | > 1.0E+14 ohms·cm | |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| dielectric constant | 60 Hz | ASTM D150 | 3.30 |
| Dissipation Factor | 60 Hz | ASTM D150 | 2.0E-3 |
| 50 Hz | ASTM D150 | 2.0E-3 | |
| dielectric constant | 1 MHz | ASTM D150 | 3.10 |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.020 |
| dielectric constant | 50 kHz | ASTM D150 | 3.30 |
| physical property | Test Condition | Test Method | SABIC EU/XL1339U-BK1370 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.70 % |
| Shrinkage rate | 横向流动 | 内部方法 | 0.50 - 0.80 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.10 % |
| Shrinkage rate | 流动 | 内部方法 | 0.50 - 0.80 % |
| Melt volume flow rate | 265°C/1.2 kg | ISO 1133 | 4.00 cm3/10min |
| Water absorption rate | 平衡, 50% RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | SABIC EU/XL1339U-BK1370 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 135 °C |
| Linear coefficient of thermal expansion | 流动 : -30 到 30°C | ASTM D696 | 7.6E-5 cm/cm/°C |
| thermal conductivity | ASTM C177 | 0.18 W/m/K | |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Be | 125 °C |
| vicat | -- | ISO 306/A50 | 140 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Ae | 105 °C |
| vicat | -- | ISO 306/B50 | 130 °C |
| Linear coefficient of thermal expansion | 横向 : -30 到 30°C | ASTM D696 | 7.9E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SABIC EU/XL1339U-BK1370 |
|---|---|---|---|
| screw speed | 50 to 80 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| drying temperature | 110 °C | ||
| Suggested injection volume | 50 to 80 % | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature in the middle of the barrel | 250 to 270 °C | ||
| Temperature at the rear of the barrel | 245 to 265 °C | ||
| Exhaust hole depth | 0.013 to 0.020 mm | ||
| Temperature at the front of the material cylinder | 255 to 275 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 65 to 90 °C | ||
| Spray nozzle temperature | 255 to 270 °C |